The present work deals with the design and construction of an equipment for studying the drying process of gels and solids. The equipment was built using mainly a commercial oven and others peripherals for programmed control of temperature, humidity and data acquisition. The system allows the in situ monitoring of the gel drying, registering the weight loss, and the shrinkage of sample and the oven temperatures. This set of allowed parameters makes possible to establish the main steps involved in the drying of meso and nanostructured porous materials.

SnO2 thin layers, prepared from aqueous colloidal suspensions by the sol-gel process, have been dip-coated on commercial borosilicate glasses. The effect of the conditions of deposition on the optical and structural characteristics of the thin layers was analysed by UV-Vis spectroscopy, x-ray reflectometry and electron scanning microscopy. Layers prepared with withdrawal speed in between 0.1 and 10cm/min show thickness smaller than 90nm, roughness of the order of 2nm and transmittance higher than 80%, resulting in good optical quality samples. The roughness increases from 2 to 11nm as the withdrawal speed increases from 10 to 80cm/min, what seems to be associated to the enlargement of the layers thickness (> 90nm). The measurements of mass loss, done after etching with fluoridric acid show that the coated samples are more corrosion resistant than the uncoated borosilicate glass.